SIS1105岳陽巴陵石化熱塑性彈性體（苯乙烯-異戊二烯嵌段共聚物）
牌號：SIS1105?????????????
產品性能
外觀：白色或淺色，不含機械雜質及油污
結構：線型
密度：880～930kg/m3（20℃）
SI含量（%）：0
嵌段比SI：15/85
揮發份（質量分數) %：≤0.70
25度、25%甲苯溶液粘度（mPa.s）：1100-1600
拉伸強度（≥MPa）：12
扯斷伸長率（≥%）：1050
熔體質量流動速率（g/10min）：8.0~12
邵氏硬度（A）：35~50
主要應用領域：膠帶、標簽、塑料改性等。制備通用壓敏膠帶，初粘性好、持粘時間長。
岳陽市巴陵佳云石化有限公司長期備有現貨。
包裝：20 公斤紙塑包裝袋或520 公斤聚丙烯集裝袋
運輸：在運輸過程中，應采取措施防止日光直接照射和雨水浸泡，運輸車輛應整潔、避免包裝破損和雜物混入，不屬于危險品。
貯存：苯乙烯-異戊二烯嵌段共聚物（SIS）產品應貯存在通風、干燥、清潔并保持有良好消防設施的倉庫內。貯存時，應成行成垛整齊堆放，并保持一定行距，遠離熱源，并防止陽光直接照射，嚴禁在露天堆放。貯存期從生產之日起，一般不超過24個月。
?
?
Yueyang Baling Petrochemical thermoplastic elastomer (styrene isoprene block copolymer) sis1105
Brand: sis1105
Product performance
Appearance: white or light color, without mechanical impurities and oil stains
Structure: linetypes
Density: 880 ～ 930kg / m3 (20 ℃)
Si content (%): 0
Block ratio Si: 15 / 85
Volatile matter (mass fraction)%: ≤ 0.70
25 ℃, 25% toluene solution viscosity (MPa. S): 1100-1600
Tensile strength (≥ MPa): 12
Elongation at break (≥%): 1050
Melt mass flow rate (g / 10min): 8.0 ~ 12
Shore hardness (a): 35 ~ 50
Main application fields: tape, label, plastic modification, etc. The preparation of general pressure-sensitive adhesive tape has good initial adhesion and long holding time.
Yueyang Baling Jiayun Petrochemical Co., Ltd. has long-term stock.
Packing: 20kg paper plastic bag or 520kg polypropylene container bag
Transportation: in the process of transportation, measures should be taken to prevent direct sunlight and rain water immersion. Transport vehicles should be clean and tidy, and avoid package damage and sundries mixed in. They are not dangerous goods.
Storage: styrene isoprene block copolymer (SIS) products should be stored in a ventilated, dry, clean warehouse with good fire protection facilities. During storage, they should be stacked in rows and stacks in order, with a certain distance between lines, away from heat sources, and direct sunlight should be prevented. It is strictly forbidden to stack them in the open air. The storage period shall not exceed 24 months from the date of production. | 